Product Name |
Applications |
Comments |
Super Flux-A (Powder) |
All
purpose , low temperature flux for use in brazing both ferrous and
non-ferrous metals and alloys using silver brazing filler metals.
Begins to melt and dissolve oxides at 340°C. Fully molten at
about 600°C and provides adequate protection upto 750°C.
Excellent in hot rodding operation used to braze weld where the hot
brazing rod is plunged into the dry powder. Easy cleanup in hot
water. |
Equivalent to ESAB's Rupatam A flux |
Super Flux-A1 (Powder) |
For
applications where a dry low volatile flux is required. Recommended
for use in 650-815°C range. Excellent in hot rodding
operations. Easy cleanup. |
Equivalent to Handy Dry Flux 6040. |
Super Flux-A (Paste) |
General
purpose, low temperature flux which provides excellent adhesion and
creamy smooth consistency. For brazing all ferrous and non-ferrous
alloys. Begins to melt and dissolves oxides at 320°C, fully
molten at 600°C, it provides excellent protection of parts upto
870°C. Easy cleanup with hot water. |
Equivalent to Handy Flux (Paste) |
Super Flux Type D & DB (Slurry) |
For
automatic dispensing as controlled dabs or sprays. Same
formullations as Super Flux-A (Paste), with additives to provide a
lower (pourable) viscosity. Type DB has an additional ingredient for
use with more refactory oxides, such as in automated brazing of
carbides. |
Equivallent to Handy Flux Type D & DB (Slurry). |
Super Flux-B (Powder/Paste) |
For
brazing high chromium stainless stells, tungsten and chromium
carbides, and molybdenum alloys. Its temperature range is 600-925°C
and it is useful in applications where local overheating may occur,
as in fast induction heating. |
Equivalent to Handy Flux Type B-1 |
Super Flux-C (Powder/Paste) |
For
brazing aluminium bronze (A1-5 to 8,Cu-bal.), aluminium-silicon
bronze (A1-7, Si2, Cu-bal.) and nickle-aluminium-bronze(A1-9.5,
Ni-5, Fe-2.5, Mn-1, Cu-bal.) using silver brazing filler metals.
Active range: 600-870°C. Not recommended for use with aluminium
or titanium-base alloys. |
Equivalent to Handy Flux Type A-1. |
Super Flux-D (Powder/Paste) |
For
applications with long heating cycles as in furnace brazing. Also
useful in induction heating operations, where tendency to overheat
may exist. active range: 650-870°C. |
Equivalent to Handy Flux Type LT. |
Super Flux Hi- Temp |
Used
where brazing temperatures go into the 870-1100°C range or for
considerable lengths of time above 785°C. |
Equivalent to Handy Hi- Temp Flux. |
Super Flux-E (Liquid) |
For
Brazing in furnaces with poor atmosphere or joining jewellery parts
above 625°C. Primarily used where only a limited fluxing
ability is required. |
Equivalent to Handy Liquid Flux. |
Super Flux Hi-Temp M (Powder/Paste) |
Used in
the brazing of carbides, Stainless and alloy steels, and nickel
based alloys using copper alloy and gold alloy filler metals
requiring brazing temperatures between 900-1200°C. |
Equivalent to Handy Flux Hi-Temp M. |
Super Flux-BRS (Powder) |
For
brazing or fusion welding various ferrous and non-ferrous metals and
alloys (like cast iron, steels, brass etc.) using Cu-Zn (brass)
filler metals. |
Equivalent to ESAB's Brazotectic Flux. |
Super Flux BRZ (Powder) |
For
brazing various ferrous and non-ferrous metals and alloys using
Cu-Sn (bronze) based filler metals. |
Equivalent to ESAB's Bronzotectic Flux. |
Alumibraze-A (Powder) |
For
brazing aluminium and its alloys using A1-12%Si filler metal. |
Equivalent to ESAB's Albratectic Flux. |
Alumibraze-B (Powder) |
Similar
to above but this flux becomes active at a lower temperature thereby
minimizing damage to the aluminium base metal. Suitable for brazing
thin sections. |
Equivalent to Handy Flo-700 Flux. |
Alumiweld (Powder) |
For
welding aluminium and its alloys. |
Equivalent to ESAB's Alotectic Flux. |
Stainweld (Liquid) |
For
Welding stainless steels using niobium and other stainless steel
rods. |
Equivalent to ESAB's Botectic Flux. |
Castweld-A (Powder) |
For
welding cast iron. |
Equivalent to ESAB's Castox Flux. |
Cupopaste-A |
Copper
brazing paste for furnace brazing steels. |
|
Solderflux-A (Paste) |
For
soldering applications. Active range: 260-425°C. |
Equivalent to Handy Flux Type TEC. |
|
|
Specifications